In the present study an attempt was made to synthesize the $Al_2O_3$.$2SiO_2$ glass in which atomic ratio is Al:Si=1:1 by sol-gel process. And at such a low temperature as 55$0^{circ}C$ clear amorphous gel derived glass with Si-O-Al bonding was obtained. $Si(OC_2H_5)_4$ and $Al(NO_3)_3$.$9H_2O$ were used as the precursor and among the mutual solvents only n-butanol gave good results for the synthesis of the gel derived glass. Partial hydrolysis of TEOS with one-fold mol of $H_2O$ prior to the reaction with aluminum nitrate gave the better results., Total oxide content to the total reactants by weight was affective to the results.