This experiment was studied in the system of (1-x) CaO MgO $2SiO-Al_2O_3$ to investigate forming of solid solution. The technique empolyed was the well known water-quenching method. Differential thermal analysis of the each glass water quenched indicated that under 30 mole% $Al_2O_3$ was lowered with increasing of the amount of $Al_2O_3$ It was supposed by X-ray diffraction patterns of each specimen sintered at various temperature that only solid solution was formed under the 30mole % $Al_2O_3$ compositions solid solution and anorthite were formed at the 20mole% $Al_2O_3$ composition anorthite solid solution and spinel$(MgAl_2O_4)$ were formed over the 40mole% $Al_2O_3$ compositions. The maximum density and thermal expanison coefficient was 2.89g/cm 7.74x106./C$^{circ}$ respectively in the composi-tion of 10 mole% $Al_2O_3$ . All the specimens showed linear thermal expansion behavior. Microhardness was as high as 850kg/nm2 in the composition of 5, 10, 20 mole % $Al_2O_3$ and dielectric constant was 7.3-6.9