An attempt was made to derive a possible synthetic mechanism of Fluoro-phlogopite (Mica, 4Mg.$Al_2O_3$.$6SiO_2$.$K_2O$.$2MgF_2$) The pevention of fluorine vaporization turned out to be the key in the synthesis of Mica in question.l Consequently the quinary system of Mica was seperately synthesized ; frist 4MgO.$Al_2O_3-6SiO_2$(ternary system) was sintered at 135$0^{circ}C$ and $K_2O$ and $MgF_2$ were added and second 4MgO.$Al_2O_3-6SiO_2$.$K_2O$ (quarternary system) was heat-treated at 135$0^{circ}C$ and $MgF_2$ was added. The ternary system resulted in Proto-enstatite Cordierite and Spinel phases while Forsterite and Leucite were shown in the quarternay system . In both methods Fluoro-phlogopite was systhesized but the solid state reactions to form Mica from the ternary system and the quarternary system were different. High temperature reactions in the formation of Mica were investigated employing XRD, DTA and SEM The study of the synthesis of Mica indirectly suggested a method of phase analysis of quinary system(MgO-$Al_2O_3-SiO_2-K_2O-MgF_2$) and quarternary system(MgO-$Al_2O_3-SiO_2-K_2O-MgF_2$) at various temperatures.