The main object of this study is to investigate the effect of Al powder as an additive on the sintering of calcined alumina comparing with that of calcined alumina alone. The degree of Al oxidation is calculated by measuring the weight increase during the firing Water absorption bulk density and compressive strength of the $Al_2O_3+Al$ system at each temperature are compared with those of $Al_2O_4$ alone. The $Al_2O_3+Al$ system shows better physical propeties than Al2O3 alone and it seems by the SEM observation that the fine oxidized Al particles(fine $Al_2O_3$ particles submicron unit) fill the interstices of the original $Al_2O_3$ par-ticles and thus result in the well-close-packed arrangement of the particles.