A study was made of the effect of cold working and stabilizing temperature on the fatigue properties of Aluminum alloy 5083. The amount of cold working ranged from 14% to 35% and stabilizing temperature was 120.deg. C-160.deg. C. Rotary bending fatigue test was carried out, and it was found that 1) E specimen that had been cold worked by the cold reduction of 35% and stabilized at 160.deg. C for 2 hours was showed the most excellent fatigue limit and endurance ratio and, 2) By the results of the between crack propagation behavior and stress intensity factor, E specimen was showed the better resistance to fatigue crack growth than others.