The purpose of this study was to investigate the effects of laundry variables and additives on the removal of deposited calcium on the cotton fabric. Samples of calcium deposited fabric was made by treating fabric with $CaC1_2$ and $Na_2CO_3$ solution subsequently. The experimental variables were: 1) NaOH concentration ($0.0001\%$, $0.0005\%$, $0.001\%$, $0.005\%$, $0.01\%$) 2) Alkaline builders(sodium carbonate, sodium meta silicate) 3) Sequestering agents(STPP and EDTA concentration: $0.02\%$, $0.04\%$, $0.06\%$, $0.08\%$, $0.1\%$, $0.15\%$, $0.2\%$) 4) Temperatures($25pm1^{circ}C$, $40pm1^{circ}C$, $60pm1^{circ}C$) 5) Edge-abrasion to the removal of deposited calcium on the cotton fabric. The fabric was washed for 15 minutes in a washing machine(Model: Gold Star WP-3007) or Launder-0-meter(40$~$45 r.p.m., Toyo Rika Instrument Inc.) and rinsed 3 times per every rinsing time. The amount of calcium deposits on the fabrics was determined by EDTA-back titration methods and edge-abrasion was evaluated by ASTM D 3886 method. The results of this study were as follows: 1) pH of surfactant solution(NaOH concentration) did not influence on the removal of deposited calcium on the cotton fabric. 2) Added alkaline builders did not influence on the removal of deposited calcium on the cotton fabric. 3) It was shown that STPP and EDTA were effective to remove deposited calcium. The removal of deposited calcium on the cotton fabric was proportionally increased with increasing concentration of STPP and EDTA. At high concentration, however, the rate was rather decreased with increasing concentration. 4) The temperature of washing solution did not influence on the removal of dedosited calcium on the cotton fabric. 5) As the removal of deposited calcium on the cotton fabric was increased, the rate of edge-abrasion of the fabric was gradually increased.