Water soluble urea-melamine-phenol copolymer adhesive manufactured with 80 percent of urea resin contents was manufactured by different molar ratio for a high temperature curing type, and their properties and strengthes were examined through manufactures of plywood with Kapur (Dryobalanops spp.) veneers. The results are summarized as follows: 1. Specific gravities of air dried plywood manufactured from each adhesive ranged from 0.78 to 0.84 and their moisture contents met the KS requirement. 2. In dry and wet shear strength, $U_{80}M_{10}P_{10}$ copolymer resin showed the highest value and urea resin was the lowest, indicating that melamine and phenol were effective for increasing glue shear strength of urea resin. 3. In case of glue shear strength after boiling test, phenolic resin was the nest and melamine was not so effective as phenol on reinforcement of boiling water resistance of urea resin.