Unstabilized Zirconia was added to basic composition under 44$mu extrm{m}$ of 57.80wt% Clay-22.20wt% Chamotte-20.00wt% Agalmatolite system. Here the amount and the particle size of Zirconia were 5-25wt% and -20${mu}{ extrm}{m}$ respectively and the body of these composition was first at 135$0^{circ}C$. The results obtained from examining the properties of sintered body were as follows. 1. Firing linear shrinkage apparent density and bulk density apparent porosity and water absorption of the samples had the tend to increase according as the particle size of zirconia became larger and the amount of zirconia increased. 2. Modulus of rupture was inversely proportional to the particle size and the additive amount of zirconia, . Especially in case that the particle size of zirconia over 5${mu}{ extrm}{m}$ and the additive amount of zirconia was 25wt% the modulus of rupture had shrunk drastically. 3. The maximum value of KIC was obtained at 20wt% additive amount of zirconia according to the each particle size of zirconia. Especially the highest value of KIC is 2, 173 M. Pa. M1/2 when the particle size of zirconia is 5~10${mu}{ extrm}{m}$ and the additive amount is 20wt%