Nowdays, the high strength aluminum alloys are broadly used for structural purpose, but the practical strengthening method by aging treatment are not much available. So that, in this study, in order to investigate the effect of aging treatment for strengthening on the fracture characteristics of the domestic high strength Al alloy (A2024BE), the variations of the aging temperature and time were taken after solution treatment. By microstructural examination, and by SEM fractographs of the fractures, the effects of aging temperature and time were investigated, considering on the fracture behaviour. The results obtained are as follows: 1) It was confirmed by microstructural investigation that the aging temperature of $190^{circ}C$ and the aging time of 12hours were optimal to get more sound microstructure with distribution of uniform precipitation. 2) By step aging treatment, the proper aging time for obtaining the similar microstructure without any microstructural defects could be shortened in half the normal aging time. 3)By examining the SEM fractographs of the fracture surface, it was found that, regardless of the aging treatment time and temperature, all were intergranular ductile fractures, but the aging treatment at $190^{circ}C$ for 12 hours resulted in dimple-type-transgranular and intergranular-ductile-frature.