In general, acid dyes been used for silk dyeing, but acid dyed silk shows weakness in color fastess, To improve this defect, the silk dyed with Acid Mordant Blue 13 was treated with chromes salts solution. Some mechanical properties and dyeing behaviors of the chrome mordant with dyed silk fabric were tested in this work. The tensile strength of silk fabric treated with chrome salts solution was decreased as the duration of treatment was increased. The mean rate constant (K) of photo-degradation was 1.019, and 1.047 after treated with Cr (III) and Cr (Ⅵ), respectively, whereas it was 1.304 in untreatment. The washing fastness of silk fabric also was improved by treatment with mordant and it was 3rd-4th grade and 4th grade when silk was treated with Cr (III) and Cr (Ⅵ), respectively, while untreatment gave 1st grade. The colour of dyed silk fabric was 2.5RP.3/10, but it was 5PB.4/3 and 5PB. 4/4 when the silk fabric was treated with Cr (III) for two hours and with Cr (Ⅵ) for one hour at 90$^{circ}C$, respectively.