The self-diffusion experiment of THO was performed across a series of copolymer hydrogel membranes at different temperatures. Copolymer hydrogel membranes were prepared by copolymerizing 2-hydroxyethyl methacrylate (HEMA) and 2-aminoethyl methacrylate (AEMA) in the presence of the solvent and the crosslinker, ethylene glycol dimethacrylate (EGDMA). By changing the crosslinker content and the ratio of HEMA and AEMA monomer, two series of copolymer hydrogel membranes were synthesized. The tagging material was THO and efflux of THO was counted on a Liquid Sc-intillation Counter. The experimental data show that the permeability decreases as the amount of EGDMA and the mole fraction of HEMA increase, and the permeability is proportional to the temperature. The partition coefficient shows a parallel trend with permeability. Using the relationship between viscosity and diffusivity, the viscosity of water within the membrane was obtained. According to the result, the viscosity of watler within the membrane has the same value with those of supercooling water. And we obtained the activation energy of THO for transport in the membrane by using Arrhenius plotting.