The purpose of this study was to observe the tensile and bonding strength of the joined amalgam restoration. Amalgam alloys of fine-cut (F-type), spherical (S-type), and dispersed type (D-type) were selected in this study, and all specimens were divided into three groups according to the condensation methods as follows. Group I : the control group which condense the same kinds of mixed amalgam into the whole part of the mold respectively. Group II : the group which condense a mix of amalgam into one half of the mold, and then condense a new mix of amalgam into the rest half of the mold 15 minutes later. Group III : the group which condense a mixed amalgam into one half of the mold, and then condense a new mix of amalgam into the rest half of the mold 7 days later. All specimens were stored in incubator at $37{pm}1^{circ}C$ for seven days with immersing in saline solution before testing. The tensile and bonding strength of them were measured with Instron Universal Testing machine. The results were as follows: 1. In Group I, the order of tensile strength was F-type, S-type, and D-type. 2. In case of bonding of S-type + S-type, the difference of the bonding strength between Group II and III was not significant. (P> 0.05) 3. The bonding strength of F-type + S-type of Group II was marked the highest in value, and the lowest bonding strength was showed in bonded D-type + D-type of Group III. 4. In case of bonding with the different kinds of amalgam alloy in Group II, the specimen bonded to F-type was marked the highest bonding strength, and the specimen bonded with F-type was marked the lowest one. In Group II, the bonding strength of the specimens bonded with the same kinds of amalgam alloy was presented as the same order as that of Group I. 5. In Group III, the specimen connected with D-type marked the lowest bonding strength of all specimens. In Group III, the bonding strength of the specimens connected with the same kinds of amalgam alloy was the order of S-type + S-type, F-type + F-type, and D-type + D-type.