This Experimental study was performed to study the effect of the heat soaking and the diameter of pattern on the casting ability of three nonprecious alloys manufactured for porcelain-metal restorations, with respect to their ability to reproduce test pieces by casting over a selected range of uniform diameters. Samples of total 60 were constructed and divided into 6 groups according to the two variables, the diameter and the heat soaking. The completed cast samples were examined visually and measured with a caliper calibrated to 0.05mm. The results obtained were as follows: 1. Length cast was significantly related to the diameter to be cast, especially in the case of the marrowest diameter of 230m. 2. Length cast not significantly related to the heat soaking. 3. The completeness of casting was significantly related to the diameter to be cast, particularly in the case of the narrowest diameter of 230m. 4. The completeness of casting was not significantly related to the heat soaking. 5. All of the three nonprecious alloys used for this experiment were significantly different from an ideal alloy in the completeness of casting.