The purpose of this experiment was to study the effects of laser on a base metal alloy for dental casting. In this study, microhardness, corrosion resistance, wear resistance, interaction behavior of metal-ceramic interface, and bond strength were tested before and after the laser treatment for metal-ceramic alloy. The conclusion arised from this study are as follows: 1. The hardness of lased area was higher than that of unlased area. 2. The corrosion resistance was higher in lased specimen than in unlased specimen. 3. the wear resistance was higher in Iased specimen than in unlased specimen. 4. The EDAX showed that Mo, Si and Al were increased in lased surface but Ni and Cr not increased. 5. The SEM of lased area revealed a typical microstructure. 6. The bond strength of lased specimen was increased in 11.2% than of unlased specimen.