The apparent activation energy Q$_{c}$ and the applied stress exponent n have been determined during creep of Al 7075 alloy over the temperature range of 90.deg. C to 320.deg. C (0.4-0.65T$_{m}$) and stress range of 1.85 kgf/mm$^{2}$ to 21 kgf/mm$^{2}$, respectively in order to investigate the creep behavior. Constant load creep tests were carried out in the experiment. At round the temperature of 200.deg. C-240.deg. C and under the stress level 8.13-9.55kgf/mm$^{2}$ and again at around the temperature of 280.deg. C-320.deg. C and under the stress level of 1.85-2.55kgf/mm$^{2}$, the creep behavior obeyed for the creep deformation was nearly equal to that of the volume self diffusion of pure aluminum (34kcal/mole). But at around the temperature of 90.deg. C and under the stress level of 10-21kgf/mm$^{2}$, the creep behavior did not obey a simple power-law relation and the apparent activation enrgy, Q$_{c}$ was 26.01 kcal/mole. From the above facts, at around the temperature of 200.deg. C-240.deg. C and 280.deg. C-320.deg. C, the creep deformation for Al 7075 alloy seemed to be controlled by dislocation climb but at 90.deg. C, by cross slip over the range of experimental stress conditions.tions.