Synthetic mica $NaMg_{2.5}(Si_4O_{10})F_2 (Na-TSM)$ was treated with HCl solution and H-type exchange resin to investigate the chemical stability and the ion exchange by measuring the dissolution of chemical components and the exchanged $H^+$ ion. The replacement of $Na^+$ ion occurred in contact with HCl solution and H-type ion exchange resin at the surface of Na-TSM particles reached $Na^+$ ions at maximum value of 70~80%. $Mg^{2+}$ ion of octahedral layer became to dissolve from the pH2 solution and th amount of it dissolved in-creased almost proportional to $H^+$ ion concentration from around 0.02N $H^+$ ion equilibrium concentration. The crystalline structure of Na-TSM was destructed by dissolution of Mg2+ ion in cncentrated hydrochloric acid solution and resulted silica gel precipitation.