The structural and useful characteristics of silk habutae treated with silicone resin by emulsion finishing method were studied. The results were obtained through crease recovery test, water repellency test, scanning micrograph observation, amino acid analysis, X-Ray diffraction analysis, and Fourier Transform Infrared Spectroscopy. The results are summarized as follows; 1) The improvement in crease recovery of silk habutae finished with silicone resin, was observed b soaping treatment and curing conditions. 2) The higher water repellency and stiffness in silk fabrics finished with silicone resin was found by the fabric inspection and the scanning electron microscopic observation. It is suggested that silicone resin impregnated into the void of silk fibroin. 3) The polar side chains of amino acid composition were decreased, when the silicone resin was treated on silk fibroin. 4) Through Amino acid analysis of silicone resin finished fibroin, the different amounts of amino acid composition was indicated due to silk fibroin silicone polymer reaction and the structural difference of its fibroin were also proved by X-ray diffractograms. 5) The functionality of the siloxane compound may be deduced from the silicone finished silk habutae by Fourier Transform Spectroscopy. It was concluded from the above results that the useful characteristics of silk fabric can be improved by silicone resin finishing.