The anodic oxidations of the Silver(I) / Silver(II) / Silver(III) system have been studied in aq. 2M $AgNO_3$ solution with Platinum and Carbon electrodes. It has been found that $Ag_7O_8NO_3$ can be produced at relatively higher current density. Deposited black Oxy-salt were analyzed with several methods such as oxidizing power, X-ray powder diffraction patterns, thermal analysis, and reduction curves. It decomposed to AgO upon being suspended in boiling water. AgO compound obtained from $Ag_7O_8NO_3$ were purer and denser than Alfa-product AgO.