A study was conducted to determine the physical properties related to drying characteristics, the seasonal air drying curves and the kiln drying schedule for taun lumber imported and utilized. This kiln drying schedule was found by oven drying and developed by pilot testing of green lumber and partially air dried lumber. The results of this study were as follows; 1. Average green specific gravity and standard deviation of heartwood lumber were 0.60${pm}$0.03 and those of sapwood lumber were 0.64${pm}$0.02. 2. Radial shrinkage from green to air dry and from green to oven dry were 3.05 percent and 5.96 percent respectively, and tangential shrinkage from green to air dry and to oven dry were 5.49 percent and 8.74 percent respectively. 3. Drying time for 25mm thick green lumber (50 percent moisture content) air dried to 30 percent moisture content were 14 days in springtime. 6 days in summertime, and 12 days in autumntime, whereas for 50mm thick lumber in 36 days in springtime, 18 days in summertime, 38 days in autumntime. 4. Kiln drying schedules developed by oven drying were T8-B3 for 25mm thick lumber and T5-B2 for 50mm thick lumber. 5. Kiln drying curves of green 25mm and 50mm thick lumber were similar to those of partially air dried lumber from the level of 30 percent average moisture content. Green 25mm thick lumber (55.7 percent moisture content) was dried to 9.3 percent moisture content in 101.5 hours and green 50mm thick lumber (65.6 percent moisture content) was dried to 11.5 percent moisture content in 526 hours. 6. End checking for green 25mm thick lumber occured in 49.6 percent moisture content and reached maximum amount in 27.6 percent moisture content and closed in 15.8 percent moisture content. 7. End checking for green 50mm thick lumber and partially air dried lumber developed and reached maximum amount earlier then for 25mm thick lumber. 8. Final moisture content of surface layer for 50mm thick lumber was one half of that of core, and moisture content equalized in the lumber after nine days of room conditioning. 9. Casehardening for 50mm thick lumber was slight and was conditioned after nine days of room stroage. 10. Drying defects, such as end checking and surface checking, were not observed and the quality of dry lumber was first.