본 연구에서는 2024 Al 합금에 대하여 260-380.deg. C의 온도 범위 및 2~5kgf/ m $m^{2}$의 부과응력 범위에서 실시한 고온 정상 크리이프 변형 중의 내부응력 .sigma. $_{i}$,의탄성 변형 .epsilon.$_{A}$ 및 회복율 r의 측정 실험을 통하여 이들 상호간의 관계 를 살펴 보고자 한다.다.다.
Measurements of internal stress .sigma.$_{i}$, anelastic strain .epsilon.$_{A}$ and recovery rate .gamma. were made in steady state creep of 2024 Al alloys over a wide range of stresses at temperatures between 260.deg. C and 380.deg. C, for the purpose of investigating the relations among the three parameters. Values of .sigma.$_{i}$ were obtained by the method of strain transient dip test, and those of .epsilon.$_{A}$ and .gamma. were determined from the results of sudden stress removal or reduction tests. As a main result, it is thought that the anelastic behavior and recovery process are basically dependent on same deformation mechanisms.sms.sms.