Yttria-bismuth-stabilized zirconia was investigated with respect to the amount of $Bi_2O_3$ addition in the ran-ge of 0.5~5mol% to the base composition of $(ZrO_2)_{0.92}(Y_2O_3)_{0.08}.Bismuth was introduced into the ma-terial with $Bi_2O_3-SiO_2$ glasses in order to reduce the evaporation of components. The sinterbility evaporation of components phase formation and microstructure were evaluated depending on the amount of $Bi_2O_3-SiO_2$ glass addition. Two probe A. C conductivity measurement was subjected to all the specimens and the result was discussed on the possible substitution of $Bi^{3+}$ for $Zr^{4+}$ and interistial $Si^{4+}$ in the fluorite structure of zirconia crystal there-upon the possible change in the capability of oxygen transference within the material. It was found that the addition of $Bi_2O_3$ could improve the sinterbility of material very much while not so much.oxygen sensing material suitable for relative low temperature firing.