Yttria-antimonia-stabilized zirconia was investigated with respect to the amount of $Sb_2O_3$ addition in the range of 0.5~5mole% to the base composition of $(ZrO)_{0.92}(Y_2O_3)_{0.08}$ The sinterbility modulus of rupture Vickers hardness evaporation of components phase form-tion and mcicrostructure were evaluated with antimonia content. Also two probe A. C conductivity measurement was subjected to all specimens and the best results are achieved with 1mol% $Sb_2O_3$ as a sinter agent and relative density of~98% obtained at 140$0^{circ}C$ and this composition has a maximum electrical conductivity due to the possible substition of $Sb^{3+}$ for $Zr^{4+}$ site. The effect of $Sb_2O_3$ on the electrical conductivity of th bulk and the grain boundaries has on investigated using frequency dispersion analysis (5~106 Hz) Antimonia addition has a negative in-fluence on both the bulk and the grain boundary conductivity except for a 1 mon% addition. The additive antimonia has improve a modulus of rupture to 60~MPa due to metastable-tetragonal phase apparence and decrease the hardness with increasing the $Sb_2O_3$ content.