The calcining temperature ranging from 900$^{circ}C$ to 1300$^{circ}C$ affected on the planar coupling factor and resonance characteristics of BaTiO3 ceramics doped with 0.2 wt% MnO2 have been investigated. Dielectric constant planar coupling factor and anti-resonance frequency of the sample increased with the calcining temperature up to 1,200$^{circ}C$ and decreased above that temperature but the resonance frequency decreased slightly with the increasing calcining temperature. The planar coupling factor and anti-resonance frequency increased with the sintered density and dielectric constant while the resonance frequency was almost constant. The resonance and anti-resonance frequency increased with the sample temperature.