Corrosion fatigue fracture with change in the grain size of M.E.F. dual phase steel is investigated in 3.5% NaCI aqueous solution at pH 2, 4, 6, 9, and 11. Generally speaking, decrease in corrosion fatigue life is strongly dependent on decrease in pH and slightly on the grain size. For the B material with the big grain size, the fatigue life is small due to its large reduction ratio of corrosion fatigue life. The influence of grain size on the reduction ratio of corrosion fatigue life is large at pH 11-6. Whi9le at pH 4-2 the reduction ratio of corrosion fatigue life only depends on the corrosion effect. The larger grain size and the lass pH result in the greater influence on corrosion fatigue crack propagation rate. As pH decreases, the plateau portion in the crack propagation rate curves of the B material are distinct. Crack propagation rate curves become slow down at high .DELTA.K range because crack closure effect by minute corrosion products inside crack causes the oxidation corrosion action less effective for a certain period of time. In A material with small grain size, fatigue life is increased in proportion with increase of martensite intergranular which brings forth restraining the crack propagation decreases crack propagation rate. Corrosion pit which is created in the surface of specimen is found at pH 6,4 and 2 which is noticeable and the unevenness of the surface of the specimen becomes severe as pH decreases. The unevenness of corrosion fatigue fracture surface is severe as the effect of pH increases i.e. as pH decreases. In proportion with increase in the grain size and decrease in pH, the aspect of brittle fracture becomes evident.