The aims of this study was to determine the mechanical properties of steel-fiber reinforced concrete under direct tensile loading, and also to insestigate the mechanism fiber reinforcement in order to improve the possible applications of steel-fiber reinforced concrete. In this study the major variables of experimental investigation were fiber conntents, and the lengths and diameters of fibers. The major results obtained are summarized as follows : 1. The strength, elastic modulus and energy absorption capability of steel-fiber reinforced concrete under direct tensile loading were improved as increasing of fiber contents. 2. The direct tensile strength of steel-fiber reinforced concrete was not influenced by the lengths of fiber, but was decreased as increasing of fiber diameters. 3. The direct tensile strength of steel-fiber reinforced concrete was not influenced by the fiber aspect-ratio, but this was because the fiber contents were below the critical value of fiber content. 4. The correlation of direct tensile strength and combined parameter, Vf l/d, was not good. 5. Mutiple cracking and post-crack resistance were investigated at stress-strain curves in direct tensile test. 6. The effect of fiber reinforcement can be influenced by fiber orientation and the bond strength between fiber and matrix. 7. The improvement of mechanical properties of steel-fiber reinforced concrete under direct tensile loading can be theoretically explained by the concept of composite materials.