Glass forming ranges in the AlF3-(Mg＋Sr＋Ba)F2-P2O5 system are studied and ultraviolet transmission, infrared transmission, coefficient of refractive index, thermal expansion coefficient, density and chemical durability of the glasses are determined. Glass forming range is restricted MgF2 0-10wt%, SrF2 10-50wt%, BaF2 10-40wt% in this system. While BaF2 is substituted by SrF2, density and refractive index are decreased, micro hardness and thermal expansion coefficient are increased according to the increasing of SrF2 at fixed MgF2 contents. These samples represent high transmittance(93%) from 400nm to 3800nm and chemical durability of these samples show less than 0.3mg/$ extrm{cm}^2$$.$hy by weightloss.