There were several numbers of studies on chemically strengthening glass. Most of them were strengthened in molten salt bath below transformation range of glass. Apart from them, this study used solution hydration technique by Autoclave. After determining proper concentration of AgNO3 salt solution, experimental condition varied from 4hrs to 16hrs at relatively low temperature (180, 200, 220$^{circ}C$). The results showed that the Soda-Lime-Silica glass could be strengthened by diffusion mechanism without influence of water above 15% salt solution. Because of Ag+ ion penetration in glass surface, yellow color appeared and decreased transmittance at visible range. Modulus of rupture was increased with the amount of exchange and brittleness was decreased.