The system of 0.1Pb(Mg1/3N2/3)O3-yPbTiO3-zPbZrO3 piezoelectric ceramics was made in the radial model disk and ring dot type filter. The resonant frequency(fr) variations were investigated for 100 hours and the temperature range from 20$^{circ}C$ to 100$^{circ}C$. As the results, the morphotropic phase boundary was supposed to be the composition of 45 y 50 and 40 z 45. The best characteristic of againg effect, after 10-hours, was composed of y, z=45. The stabilized characteristic of temperature varition, to become 0.1% up to 100$^{circ}C$, was composed of y=50 and z=40. The bandwidth was broadened with increasing the electromechanical coefficient(kp), and the filter characteristics was approached ideal mode with increasing mechanical quality factor(Qm). Kp and Qm affected combinationally on filter characteristics.