TiC was deposited onto several substrate steels by the Chemical Vapor Deposition technique from TiCl4-CH4-H2 gas mixtures in the horizontal resistance furnace. Deposition rates and morphologies of the coatings were investigated with the carbon contents. Deposition thickness increased linearly with the deposition time in the Presence of CH4 gas. The various interlayers of coating by EDS and X-ray Diffraction were proved as Cr7C3 and Fe3C. Chromium contents did not affect the preferred orientation of TiC deposit. The deposition was controlled by a mass transport and a surface reaction in case of 1 wt% C-5.25 wt% Cr steel irrespective of deposition temperature.