The use of composite resin for the posterior teeth gives rise to clinical problem due to the lack of mechanical properties. The purpose of this study was to observe the fractured surfaces of light posterior composite resins which are P-10, Clearfil posterior, Adaptic anterior & posterior, P-30, Lite-fil posterior, Estilux posterior, Helio-molar, and Ful-fil com pules (Table 1). The failure of composite resin specimens of I, T and Y-Type (Fig. 1,2) occured under compression. Fractographical observations by SEM (JSM-T20, JEOL) were carried out in order to examine the fracture behaviour of eight composite resins in different types of specimens. The results obtained from this study were as follows: 1. Similar features were found in fractured surfaces of eight composite resins. 2. The crack growth was initiated at the regions of porosities. 3. The crack propagated on the filler-matrix interface. 4. As the crack increased in size, it accelerated to form secondary crack. 5. The fracture behaviour was dependent on the content, size, shape, and distribution of fillers.