This study was performed to obtain the basic data which can be applied to use of foaming mortars. The results obtained were Summarized as follows; 1.At the mixing ratio of 1:1, the highest bulk densities were showed by foaming mortars, respectively. But, it gradually was decreased in poorer mixing ratio and more addition of foaming agent. The decreasing rates of bulk densities were increased in richer mixing ratio and more addition of foaming agent. 2.The bulk densities were decreased up to 38.8-55.9% by mix-foaming type and 9.7-23.6% by pre-foamed type than cement mortar. 3.At the mixing ratio of 1:1, the lowest absorption rates were showed by foaming mortars, respectively. But, it gradually was increased in poorer mixing ratio and more addition of foaming agent. The increasing rates of absorption rates were increased in richer mixing ratio and more addition of foaming agent. 4.Absorption rates when immersed in 72hours were showed up tp 3.41-5.85 times by mix-foaming type and 1.05- 1.S5times by pre -foamed type than cement mortar, it was significantly higher at the early stage of immersed time than cement mortar. 5.The correlations between bulk density and absorption rate were highly singnificant, respectively. The multiple regression equations of bulk density and absorption rate were computed depending on a fuction of mixing ratio and addition of foaming agent. it was highly significant respectively.