This study was performed to obtain the basic data which can be applied to use of foamihg mortars. 1. At the mixing ratio 1:1, the highest strengths were showed by foaming mortam, respec - tively. But, it. gradually was decreased in poorer mixing ratio and more addition of foam- ing agent. The decreasing rates of strengths were incresed in poorer mixing ratio and more addition of foaming agent. 2. The strengths were decreased up to 77.0-92.8% by mix-foaming type and 36.7-74.4% by pre-foamed type than cement mortar. 3. At the mixing ratio of 1:1, the lowest air contents were showed by foaming mortars, respectively. But, it gradually was increased in poorer mixing ratio and more addition of foaming agent. The increasing rates of air contents were increased in richer mixing ratio and more addition of foaming agent. 4. Air contents were showed up to 26.0-63.8 times by mix-foaming type and 5.8-17.7 times by pre-foamed type than cement mortar, respectively. 5. The correlations between compressive strength and air content were highly significant, respectively. The multiple regression equations of strengths and air content were computed depending on a fuction of mixing ratio and addition of foarning agent. It was highly significant, respectively.