Yttria-Stabilized Cubic Zirconia Crystals with Various Y2O3 amounts (6-15mol%) were grown by the Skull melting technique. The modeling of the nucleation at the Skull bottom and the best growth condition were studied. The abrupt changes in generator heating Power and lowering rate of crucible caused the dendritic growth in the grown crystal. The optimum condition of cubic Zirconia single crystals was obtained when the lowering rate was gradually increased. The effect of Y2O3 amounts on the perfection adn the color of the grown crystal were determined. The darkish color generated in the crystals added Y2O3 amounts over 12mol% was eliminated by the annealing in air at 1200$^{circ}C$ for 24hrs.