The properties of scid-resistance to boiling HCl, thermal expansion coefficient and softening temperature of mother glass and glass-ceramic of LAS systems were investigated at the contents of SiO2 varing from 57 to 67wt%. The nucleation and growth of crystalline phase of LAS compositions were carried out at 50$0^{circ}C$ and $700^{circ}C$. The crystalline phase jconsists of lithium alumino silicate, lithum meta silicate, lithium disilicate, $alpha$-crystobalite and $alpha$-quartz. Lithium alumino silicate(virgilite) is the major crystalline phase in the glass ceramics. The degree of acid resistant property was increased in proportion with the silica content for both glass and ceramics. Glass-ceramic gives lower acid-resistance and thermal expansion coefficient while softening temperature shows higher for glass-ceramic than for mother glass.