Te-thin films were highly proper material for optical recording media, but has the demerit of short archival life time due to the unstability to humidity. In order to restrain the degradation, Te$_{100-x}$Se$_{x}$ alloys adding Se stable for the humidity were fabricated. Primarily, to measure the degradation rate with varing the composition of Se to x=5, 10, 14, 25 at.% at Te$_{100-x}$ Se$_{x}$, the change of light transmittance was used in various temperature-humidity environments. As the results, it was showed that Se$_{86}$Te$_{14}$ thin was the most proper composition for the improvement of degradation restraint.int.int.