$SnO_X$/Pt 薄膜형 가스感知素子의 製造하고 그 특성을 결정하였다. $SnO_X$/Pt 薄膜은 $SnO_2$에 Pt를 重量比로 2% 섞은 표적을 電子량 加熱승치法으로 形成하였다. 素子의 전도도는 온도의존성을 보였고, CO 가스에 대한 感度는 2000 ppm 이하의 낮은 농도범위에서 가스농도는 평방근에 비례하였다. 최적동작온도는 약 300$^{circ}$C 였고 CO 가스농도가 5000 ppm에서의 응답시간은 약 20초 였다.
$SnO_X$/Pt thin film gas sensors were fabricated and their performance characteristics were measured. The $SnO_X$/Pt films were deposited by vacuum evaporating the $SnO_2$ target mixed with 2 wt% Pt. The conductivity showed the temperature dependence and the sensitivity to CO gas was proportional to the square root of gas concentration below 2000 ppm. The optimum operating temperature of the fabricated devices was about 300$^{circ}$C and the response time in 5000 ppm CO gas was about 20 sec.