The purpose of this study is to evaluate the pulpal responses to the base materials such as zinc oxide eugenol cement, calcium hydroxide, zinc phosphate cement, polycarboxylate cement and glass ionomer cement. The 100 caries free dog teeth were devided into 2 groups by remaining dentin thickness (Group A: 0.4-0.6 mm, Group B: 0.8-1.0 mm) and each group were devided into 5 subgroups. The intervals of observation period are 3days, 1 week, 2 weeks, 4 weeks and 8 weeks respectively after experiment. The specimens were fixed with 10% formalin and decalcifed in 5% nitric acid. All specimens were stained with Hematoxylin-Eosin and examined histopathologically. The results were as follows. 1. In group A, atropy or hyperplasia in odontoblasts were seen in zinc oxide eugenol cement, calcium hydroxide and zinc phosphate cement. No changes in odontoblasts were seen in polycarboxylate cement and glass ionomer cement. 2. In group A, increase of predentin were seen in all experimental materials. 3. In group A, vascular congestion were seen in all experimental materials and inflammation were seen on 3 days in zinc oxide eugenol cement, 8 weeks in zinc phosphate cement and hemorrage were seen on 3 days in zinc phosphate cement. 4. In group B, changes of odontoblasts were not seen all experimental materials. 5. In group B, increase of predentin and vascular congestion were seen in all experimental materials but inflammation were not seen.