An investigation was carried out to compare the pulp responses against a few type of composite and streptococcus mutans contamination under the zinc oxide eugenol cement, and also confirmed pulpal responses of various composites with or without base. Seventy eight teeth from 6 dogs were employed and divided into 6 groups. Class V cavities were prepared on each tooth routinely with low speed dental engine. Paper disc about 0.3mm thick was immersed in the BHI broth in which streptococcus mutans had been enriched and the disc was inserted on the cavity floor prior to filling. Scotch bond puls Silux as Bis-GMA system composite resin and Helimolar as urethane system composite resin were adopted. Control group: Zinc-Oxide Eugenol cement filling Experimental groups: Group 1. Scotch bond + Silux filling with Dycal base Group 2. Heliomolar filling with Dycal base Group 3. Scotch bond + Silux filling without base Group 4. Heliomolar filling without base Group 5. Streptococcus mutans application. All cavities were sealed with thick ZOE cement to avoid marginal leakage. Postoperative intervals of 1, 2, 3, 4, 5 and 6 weeks teeth were carefully extracted, processed and stained with Hematoxylin and Eosin. The results were as follows: 1. S. mutans application group and composites without any base showed more severe pupal response than control group and dyca based groups. 2. The experimental group of S. mutans application showed severe response in the early stage compared to the two groups of composite resin without base, but no significant difference was found following periods. 3. The difference of pulpal response is not significant between Bis-GMA system and urethane system. 4. Streptococcus mutans application group and composites without base groups showed the evidence of histologic recovery at the six week cases and the large amount of reparative dentin was the prominent feature. 5. Pulp responses against every material were inclined to normal according to the time elapsed.