This study was carried out to manufacture bark board from oak bark by new processes and to examine the physical and mechanical properties of the board. This process with no addition of adhesive used higher pressure and temperature than the conventional one and was applied with or without paraformaldehyde. The results are as follows: 1. The new manufacturing process allowed a good bark board with high absorption coefficient. 2. The best manufacturing process for the mechanical properties of bark board was paraformaldehyde 10%-$250^{circ}C$-100kg/$cm^2$-3 minutes, (bending strength 40kg/$cm^2$, internal bonding strength 2kg/$cm^2$) and the best manufacturing process for both the mechanical properties of bark board and economic point of view was $250^{circ}C$-100kg/$cm^2$-3 minutes (bending strength 28kg/$cm^2$, internal bonding strength 1.52kg/$cm^2$). 3. Bark board showed specific gravities from 0.94 to 1.03 and air dried moisture content 9.2% to 11.7%, but Bark board needed paraffin wax emusion treatment. 4. The absorption coefficient of bark boards had two peaks along with frequency; one in 200-400 cps, the other 1200-2000 cps. The former was low but the latter great.