The furnace brazing in a Ar of copper to martensitic stainless steel(13.5Cr) using Cu-(5~8%)P-(0~8%)Sn powders was investigated. Shear strength, wettability, reacted layer, defect ratio at the stainless steel interface was evaluated. As Sn was added to the Cu-P powders, defect ratio and P content at the stainless steel interface decreased. And also as Sn was added, defect form at the stainless steel interface changed from the continuous layer to the discrete type, and shear strength of the brazed joint increased.