The purpose of this study is to investigate the corrosion fatigue crack growth of PWTHT specimens(SS41, SM53B) which are the compact tension ones extracted from the muti-passed weldment and weld block. The corrosion fatigue test was done at the cyclic stress frequency of 3Hz in 3.5% NaCl solution. The results are as follows. 1. Corrosion fatigue crack growth of as-weld was slower than that of base metal. 2. In the low .DELTA.K region, the effect of corrosion environment on crack growth was obvious. However, the corrosion effect decreased with the .DELTA.K slowly. 3. The behaviour of fatigue and corrosion fatigue crack growth depended on the material, heat treatment as well as experimental conditions. 4. Corrosion fatigue crack growth of PWHT specimens(SS41, SM53B) subjected to 1/4hr, was increased compared with that of as-weld. 5. There was a tendency that the exponent value(m) obtained in 3.5% NaCl solution was decreased in comparison with that in air, and the material constant(C)was increased for Paris equation, da/dN=C((.DELTA.K))$^{m}$ , compared with that in air considerably.