The effect of non-metallic inclusions on the HAZ hydrogen induced cracking was investigated. Quench and temper high tensile strength steels containing various sulphur contents were employed. The sulphur contents range between 0.007% and 0.040%. Non-metallic inclusions were mainly MnS type sylphide and Mn-Al-Si type. The sensitivity of HAZ delayed cracking was evaluated by implant testing. Diffusible hydrogen content was varied by controlling the moisture absorbing condition of manual arc welding electrodes. The one was asreceived condition, the other was dipping the electrodes in the water for ten minutes. The main results obtained were as follows; 1) The results of implant test showed that critical stress increased with increasing S content up to 0.013%. But steel containing 0.040%S showed lower critical stress than that of 0.013% S. These result suggest that there will be optimum S content to prevent HAZ delayed cracking of high strength steels. 2) Under the lower D.H.C. level, critical stress was increased with rolling reduction, but higher D.H.C. level, effect of rolling reduction was not recognized.