The characteristics of aging of near-equiatomic Ni-Ti alloy has been studied by the three point bend test and the measurement of Differential Scanning Calorimetry(DSC). The DSC is used to measure precise transformation temperatures and the amount of thermal energy required for the corresponding phase transformation. The effort of hardness on aging treatment in saline solution of $37^{circ}C$ was higher for the annealed than solution treated specimens. As the testing temperature inc- rease from under $M_f$ to above $A_f$ temperature, the elastic stiffness increased. Almost full recovery can be achieved after bending below Belo outer fiber strain. Total bend recovery decreased gradually as aging time and bend angle is increased.