In 1968, Carpentier and his associates introduced glutaraldehyde as a compound for preparing cardiac tissue valve, and this technique has provided a considerably more suitable and durable tissue valve substitute. To increase further durability of valve tissue, Reis and his colleagues designed a flexible stent to reduce the stress on the heterogeneous tissue valve mounted. However with the advent of more innovative mechanical valve currently, many bioprosthetic valves are being substituted by mechanical valves at our department of cardiothoracic surgery because of bioprosthetic valve failure. Main cause of bioprosthetic valves failure were calcification or/and tear of tissue valves. The purpose of this retrospective study is to clarify the relationship between the patients clinical profile during implantation of tissue valves and pathologic features of the failed bioprosthetic valve. From March, 1982 through June, 1988, 53 bioprosthetic heart valves that had been ex-planted from 45 patients at the department of cardiac surgery of Yonsei University Hospital were subjected to this study. The patients were 10 to 65 year-old [mean age: 30.3 yr] with 17 males and 28 females. Re-replacements of prosthetic valves were carried out twenty nine in mitral position, eight in aortic position and eight in both aortic and mitral position simultaneously. The grading and location for calcification of valves were verified by radiograms. The calcification of the explanted valves leaflets was graded from 0 to 4 plus according to Cipriano and associates method. The types of tear and perforation of leaflet were classified into four types as Ishihara has adopted initially in 1981. In younger age group under thirty three years, explanted tissue valves were significantly more affected in terms of grades of severity of valve calcification as compared with older age group [p < 0.035]. Valve calcification appeared more severe in male as compared to female [p< 0.002]. Ionescu-Shiley bovine pericardial bioprosthetic valves showed more severe calcification than Hancock porcine tissue valves [p< 0.035]. Calcium deposit was found very prevalent at the area of commissural attachment [86 % of all]. Type I of valve rupture was shown to be related with simultaneous calcification. However, the relation of explanted valve position, duration of implanted prosthetic valve, atrial fibrillation and anticoagulant therapy to the severity of bioprosthetic valve calcification were not significantly clear statistically [p > 0.05].