When some kinds of inhibitors, i.e. $1{ imes}10{-3}mol/l$ arsenic trioxide, 0.2 mol/l 2-mercaptoethanol, 0.2mol/l thiourea were added to 3% NaCl solution, there were some considererable effects to decrease corrosion current density in natural potential condition and the effect fo solution temperature increasing corrosion rate was smaller than that of no addition to 3% NaCl solution. However the susceptibility of hydrogen embrittlement due to over-protection in case of cathodic protection was much greater than that of no addition, especially was the greatest in case of addition of 2-mercaptoethanol. Therefore adding inhibitors for anti-corrosion effect, it is suggested that selection of the optimum protection potential is important from the view point of prevention against hydrogen embrittlement due to over-protection in case of cathodic protection.