The effects of composition ratios and sintering conditions in Co1-xMgxO ceramics on the sintering characteristics, electrical properties and oxygen sensing characteristics were investigated. In the same sintering conditions, porosity decreased with increase of MgO contents. The relationshiop of temperature and resistance in Co1-xMgxO ceramics showed NTC(negative temperature coefficient) characteristics at the temperature range from $700^{circ}C$ to 1,10$0^{circ}C$. In the case of pure CoO, however, the PTC(positive temperature coefficient) characteristics were shown over about 90$0^{circ}C$. The electrical conductivity of Co1-xMgxO ceramics decreased proportionally with decrease of oxygen partial pressure at the range from 1 to 10-4(atm). Particularly, Co0.5Mg0.5O ceramics showed the highest sensitivity to oxygen gas.