Synthesis of spinel pigment on ZnO-Fe2O3 system. The object of this research is the synthesis of new spinel pigments on the basic of ZnO-Fe2O3 system which was substituted by ZnO-Fe2O3 by MgO-Al2O3. This research was progressed by measuring the X-ray diffraction and the reflectances of the substitued ZnO-Fe2O3 group. Which was obtained by sintering at the temperature of 1,00$0^{circ}C$, 1,10$0^{circ}C$, 1,20$0^{circ}C$ and 1,25$0^{circ}C$ and them by regrinding. In order to coloring test, here basic compositions of Barium glaze, Zinc glaze, Lime glaze, Lead glaze and Talc glaze used in this experiment are obtained from the ceramic work. Adding synthetic stains in these basic glazes with 3%, mixing and glazing on the specimen. The specimens was fired at 1,28$0^{circ}C$ in reducing and oxidizing atmosphere in the gas kiln. The results of the research as follow. 1. Many kinds of spinel pigment was produced on ZnO-Fe2O3 system that is to say, not always only spinel. 2. Spinel peak was observed strongly on the ZnO-Fe2O3 system withsubstituting by MgO-Fe2O3 and MgO-Al2O3 group(the ratio of MgO, Al2O3 being increased, observed more strongly). 3. The most effective temperature ranges was 1,20$0^{circ}C$~1,25$0^{circ}C$. 4. The color of spinel pigments on this system was observed by "stable YR". 5. It was yellow red in oxidizing and green in reducing atmosphere on the coloring test.ring test.