The sintering behavior and grain growth of ZnO in 99.0mol% ZnO-1.0mol% Bi2O3 which are the basic compositions of ZnO varistor were studied. The microstructrual observation confirmed that the final sintered density was mainly determined at the initial stage of sintering, i.e. grain rearrangement and grain growth which were induced by the penetration of eutectic melts formed at eutectic temperature(74$0^{circ}C$). But when the liquid penetration was terminated, the grain growth did not promote further densification. Activation energy of the grain growth of ZnO in the system of 99.0mol% ZnO-1.0mol% Bi2O3 was 44.8$pm$1.8Kcal/mol.