6H-SiC is a promising material (Eg=3.0eV) for blue light-emitting doide and high-temperature semiconducting device. In the experiment, single crystals of a-SiC have been grown by the sublimation method to fabricate blue light~emitting diode. During the growth of a-SiC single crystals, a temperature Vadient, yonh temperature and pressure ranges were kept 44℃/cm , 1800-1990℃ and 50-1000 mTorr, respectively. Single crystals obtained in Acheson furnace were used as seed crystals. Polarizing microscopy and back-reflection X-ray Laue diffraction showed that the a-SiC crystal was epitaxially and on the seed crytal. It was found by XRD analysis that when other growth conditions were the same, a-SiC was grown at the temperature above 1840℃ and 3C-SiC was gown at lower temperature or under low supersaturation of vapor. The carrier type. concentration and mobility were measured be hole(p-type), 7.6x1014cm-3 and 19cm2V-1sec-1, respectively, by van der Pauw method.