The electrical conductivity of SrTiO3 thick films, which has been prepared by screen printing and sintering on polycrystalline Al2O3 substrates, was determined as a function of oxygen partial pressure and temperature. The data showed that electrical conductivity was proportional to the -1/4th power of the oxygen partial pressure for the oxygen partial pressure range from 10-4-10-8 to 10-20 atm and proportional to Po2+1/4 for the oxygen partial pressure range from 10-6-10-4 to 1atm. And then n-p transition region of electrical conductivity moved to lower oxygen partial pressure region as the sintering temperature of thick film specimens increased under about 140$0^{circ}C$. These data were consistent with the presence of small amounts of acceptor impurities in SrTiO3 thick film which have been diffused from Al2O3 substrate in the range of solid solubility limit.